Ti2 | 3.7035 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Range of Application | Standard Status | Country | Predecessor | Remark | Application temperature [°C] |
|---|---|---|---|---|---|---|---|---|
| 3.7035 (VdTÜV WB 230-3 : 2018-06) | 3.7035 | VdTÜV WB 230-3 : 2018-06 | Supersedes VdTÜV WB 230-3 : 2013-12 | Valid | Germany | Ti2 | Titanium for pressure equipment requiring monitoring acc. to AD 2000 W0, directive 2014/68/EU and for nuclear engineering. | -10 - 300 |
Chemical Composition
| C [%] | Fe [%] | H [%] | N [%] | O [%] | Source | Remark |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur |
Mechanical Properties
| Semi-finished Product | Condition | Condition Number | Designation of the delivered Condition DIN | Strength Abbrevation | Nominal Size [mm] | Temperature [°C] | Specimen Direction | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Yield Strength (1.0% offset) [MPa] | Elongation A [%] | Reduction of Area [%] | Hardness HB | HBW | Source | Remark |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Physical Properties
| Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Mean Coefficient of Thermal Expansion [10^-6*K^-1] | Thermal Conductivity [W/(m*K)] | Specific Electrical Resistance [µΩm] | Mean Specific Heat Capacity [kJ/(kg*K)] | Source |
|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
Young's Modulus [GPa] vs Temperature [°C]
Exclusive Insight Locked!
This premium diagram is currently blurred. Gain full access to detailed insights and stay ahead with exclusive content.
Unlock NowWelding and Joining
| Procedure | Welding and Joining - Evaluation | Added Materials | Source | Remark |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Heat Treatment
| Heat Treatment | Temperature [°C] | Holding Time [h] | Medium | Source |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| SB-265 Grade 2 | USA | ASME SB-265 |
| SB-338 Grade 2 | USA | ASME SB-338 |
| SB-348 Grade 2 | USA | ASME SB-348 |
| R50400 | USA | UNS |
| Ti Grade 2 | USA | |
| Titanium Grade 2 | USA | |
| 3.7035 | Germany | VdTÜV WB 230/3 |
| Titan |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| 3.7035 | Albert Hoffmann GmbH, Eschweiler |
| 3.7035 | Chr. Höver & Sohn GmbH & Co KG, Lindlar |
| Ti2 | Rosswag GmbH, Pfinztal-Kleinsteinbach |
| KS 50 | Kobe Steel Ltd., Takasago |
| Ti2 | Ningxia Orient Tantalum Industry Co. Ltd, Ningxia |
| ST-60 | Nippon Steel Ltd., Naoetsu Works |
| TIMET 3.7035 | Timet Germany GmbH, Düsseldorf |
| TIMETAL 50 A | Timet Germany GmbH, Düsseldorf |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Ti2 (3.7035; VdTÜV WB 230-3 : 2018-06)
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Poisson's ratio |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Electrical resistivity
| Temperature [°C] | Specific electrical resistance [µΩm] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
Specific heat
| Temperature [°C] | Specific heat [kJ/(kg*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Thermal conductivity
| Temperature [°C] | Thermal conductivity [W/(m*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| WIAM Material | Source description |
|---|---|
| blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Ti2 (soft annealed (+A); not specified)
Strain life
| Temperature [°C] | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| Treatment | Failure criteria | Source description |
|---|---|---|
| blur | blur | blur |
Ti2 (soft annealed (+A); rod; 6.000-100.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
Ti2 (soft annealed (+A); forging; 10.000-100.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
Ti2 (soft annealed (+A))
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| Treatment | Source description |
|---|---|
| blur | blur |